aluminum for body
« on: May 08, 2013, 01:45:32 PM »
 Wondering if everyones running .040 thickness for bodt work? Was told to use 5052 and .040. Looking at using .030 in cpl areas to cut weight. Not much but hey its weight. Eventually it will be mostly carbon fiber anyway so long life is not big issue.
Logged
Relecting obama is like shooting right foot because it did not hurt enough when you shot left foot

Offline rooman

  • Moderator
  • Hero Member
  • *****
  • Posts: 559
    • View Profile
  • Your Best Time: 6.200/222.05 (1/4 mile--NT/F)
Re: aluminum for body
« Reply #1 on: May 09, 2013, 03:20:17 PM »
I use .040" 5052 for the sides and belly pan and .050" 3003 for the cowl. I used to use 5052 for everything but Tom Hanna convinced me to use the 3003 and he is right--it is a lot easier to form the windshield opening etc.

Roo
Logged
Yeah, I am from the south--any further south and I would have been a bloody penguin.

Offline wideopen231

  • Hero Member
  • *****
  • Posts: 1911
    • View Profile
  • Your Best Time: 1/8 3.70@ 198 1/4 5.78@245
  • Your Engine: Hemi 526 ci alcohol
  • Your Track: Piedmont
  • Your Vehicle: 225 CMC FED
  • General Location: NORTH CAROLINA
Re: aluminum for body
« Reply #2 on: May 10, 2013, 09:30:55 AM »
Rooman

  So do use 5052 everywhere else or do you now use the 3003?  How about for the chute body,seems 3003 would be the way to go there if it forms easier.

 Would be kind of hard to argue with Hanna on fabrication,heck of connection you have there.Not many people can totaly amaze me but his work does.
Logged
Relecting obama is like shooting right foot because it did not hurt enough when you shot left foot

Offline rooman

  • Moderator
  • Hero Member
  • *****
  • Posts: 559
    • View Profile
  • Your Best Time: 6.200/222.05 (1/4 mile--NT/F)
Re: aluminum for body
« Reply #3 on: May 10, 2013, 12:56:49 PM »
I use the 3003 for the cowl, upper forward panels/nose and the tail. All the simple stuff is 5052.
I scored a few points with Hanna when I built Brendan Murry's current NT/F car as I tried to make it as retro as possible and he seemed to appreciate the effort. Tom was very helpful when I was re-creating his work on the clone of the Commanche that I built for Ernie Broughton. He spent quite a bit of time walking me through the configuration of the lower panels and belly pan.

Roo
Logged
Yeah, I am from the south--any further south and I would have been a bloody penguin.

Offline janjon

  • Full Member
  • ***
  • Posts: 208
    • View Profile
  • Your Best Time: 5.74/124 1/8
  • Your Engine: SB Chev, gas, 350ish
  • Your Track: Houston Motorsports Park
  • Your Vehicle: '65-ish 150" SBC/Glide FED
Re: aluminum for body
« Reply #4 on: May 12, 2013, 11:45:05 AM »
From a fabrication and craftsmanship standpoint, if there were anybody I would wish to be, it would be Tom Hannah. Mucho kudos to Rooman, too.
Logged
Just keep the same amount of stuff on the right
as there is on the left. Seeing straight ahead is highly overrated....
Pages: [1]   Go Up
« previous next »